Filter Materials

Home / Products / Fiberglass / Filter Materials

Filter Materials

Categories

Non-woven Fabric

PET Spunbond Nonwoven Fabric

PET Continuous Filament Polyester Nonwoven Fabric

PET Staple Fiber Nonwoven Fabric

Bicomponent Coarse Denier Nonwoven Fabric

Fiberglass/PVC/Polyester Mesh Fabric

Needle-Punched Nonwoven Fabric

Spunlace Nonwoven Fabric

PVC/PE/PU Coated & Laminated Nonwoven Fabric

Stitchbonded Nonwoven Fabric

PP Spunbond Nonwoven Fabric

Water-soluble Nonwoven Fabric

Fiberglass Coating Mat

Fiberglass Tissue/Veil/Mat

Fiberglass Products

Aluminum Foil Fiberglass Cloth & Tape

Filter Materials

Fiberglass Mesh

Film-Forming Agent/Binder

Stiffening Agent

Setting Agent / Fixative

Hydrogen-containing Silicone Oil

Polyferric Sulfate (PFS)

Sodium Metabisulfite

Featured Products

China Manufacturer Direct Supply Pet Spunbond Nonwoven Fabric for Home Textiles

30μm Glass Fiber Filter Paper

JRS-3075 liquid filtration media is constructed from premium high‑performance microfiberglass. It is specially engineered to effectively remove micron and submicron particles from various fluids, ensuring absolute retention efficiency of critical contaminants while providing outstanding particulate holding capacity.

CONTACT NOW

☉ Technical Data

	Unit	Max	Target	Min	Test Method
BASIS WEIGHT	(g/㎡)	80.0	75.0	70.0	GB/T 451.2-1989 TAPPI 410 om-2002
Thickness (50 kPa)	(mm)	0.520	0.460	0.400	GB/T 451.3-2002(50kpa) TAPPI 411 om-2015(50kpa)
@5.33cm/s-32 L/ min	(mm H2O) (Pa)	/ /	1.0 9.8	/ /	ATI-100XP Automated Filter Test
Air Permeability	(cfm)	/	120	100	TAPPL T 251 (125 pa)
TENSILE STRENGTH-MD	(kN/m)	/	1.400	0.800	GB/T 12914-2008 (25.4mm/ min) TAPPI 494 om-2013(25.4mm/ min)
TENSILE STRENGTH-CD	(kN/m)	/	0.800	0.400	GB/T12914-2008 (25.4mm/ min) TAPPI 494 om-2013(25.4mm/ min)
GURLEY STIFFNESS-MD	(mg)	/	1020	750	TAPPIT-543-94
Max. Pore Size	μm	/	70	/	QC/T 974-2007 ASTM F316-03
EFFICIENCY (BETA-200)	μm		30		ISO 16889(test run to 200 kPa) ISO 16889(200 kPa)
DUST HOLDING CAPACITY	(g/㎡)		140		ISO 16889(test run to 200 kPa) ISO 16889(200 kPa)

☉ Application Scenarios

1. Hydraulic oil filtration

2. Lubricating oil purification

3.Transformer oil filtration